WEICON 10012232 Ceramic W Plastic Metal (0.5Kg)
The epoxy resin system WEICON Ceramic W provides high wear protection and high abrasion resistance. It is chemical-resistant and has a high temperature resistance up to +230 °C; for a short period of time even up to +250 °C. Ceramic W is non-sagging, can be spread with a spatula. It can be applied on vertical surfaces and even overhead. It is suitable for the bonding or lining of aluminium oxide stones in mill construction, for the lining of heavily stressed pump housings, as wear protection for slide bearings, slides and pipes and wherever darker-coloured products are not suitable for optical reasons. The product can be used in machine and system construction, mill construction, apparatus engineering, and in many other industrial areas
Specification
Name
WEICON 10012232 Ceramic W Plastic Metal (0.5Kg)
SKU
4024596015848
Brand
Condition
New
| Material Properties – Epoxy (Aluminium Oxide Filled) | |
|---|---|
| General Characteristics | |
| Base | Epoxy |
| Filler | Aluminium oxide |
| Texture | Pasty |
| Colour | White |
| Processing | |
| Processing temperature | +15 °C to +40 °C |
| Component temperature | > 3 °C above dew point |
| Relative air humidity | < 85 % |
| Mixing ratio by weight | 100:25 |
| Mixing ratio by volume | 100:26 |
| Viscosity of the mixture at +25 °C | 120,000 mPa·s |
| Density of the mixture | 1.9 g/cm³ |
| Consumption (1.0 mm layer) | 1.9 kg/m² |
| Max. layer thickness per step | 10 mm |
| Curing | |
| Pot life at 20 °C, 500 g batch | 120 min |
| Additional layer after (35 % strength) | 5 h |
| Working strength after (80 % strength) | 7 h |
| Final strength (100 % strength) | 24 h |
| Shrinkage | 0.27 % |
| Mechanical Properties (24 h RT + 14 h @ 120 °C) | |
| Tensile strength (DIN EN ISO 527-2) | 54 MPa |
| Elongation at break (DIN EN ISO 527-2) | 0.5 % |
| E-modulus (tensile, DIN EN ISO 527-2) | 9,400 – 10,000 MPa |
| Compressive strength (DIN EN ISO 604) | 135 MPa |
| Bending strength (DIN EN ISO 178) | 89 MPa |
| Hardness (Shore D, DIN ISO 7619) | 91 ± 3 |
| Adhesive strength (DIN EN ISO 4624) | 17.7 MPa |
| Taber Test (DIN ISO 9352, H18, 2×1 kg, 1000 rotations) | 1.5 g / 0.8 cm³ |
| Lap Shear Strength (DIN EN 1465, 1.5 mm thickness) | |
| Steel 1.0338 sandblasted | 12 MPa |
| Stainless steel V2A sandblasted | 12 MPa |
| Aluminium sandblasted | 8 MPa |
| Galvanized steel | 2 MPa |
| Thermal Parameters | |
| Temperature resistance | -35 °C to +230 °C (briefly up to +250 °C) |
| Tg after curing at RT (DSC) | ~ +50 °C |
| Tg after tempering at 120 °C (DSC) | +107 °C |
| Heat deflection resistance (DIN EN ISO 75-2, after tempering) | +97 °C |
| Thermal conductivity (DIN EN ISO 22007-4) | 1.01 W/m·K |
| Heat capacity (DIN EN ISO 22007-4) | 0.98 J/(g·K) |
| Electrical Parameters | |
| Resistance (DIN EN 62631-3-1) | 7 · 10¹⁴ Ω·m |
| Magnetic | No |
| Approvals / Guidelines | |
| ISSA Code | 75.509.26/27 |
| IMPA Code | 812941/42 |
| MIL-Spec | Comply with MIL-C-24176 |