WEICON Casting Resin MS 1000 is a transparent and very flowable epoxy resin system with high mechanical strength. It is suitable for a wide range of applications. MS 1000 adheres well to metal, wood, rigid foam and many plastics. It can be used for large-surface adhesive bonding or for laminating composite threaded bushes and screws. Due to its low viscosity, the epoxy resin system is also suitable for the casting of electric components. It can be used for the production of fibre composites, in tool and mould making, in the electrical industry, in machine construction, and in many other industrial fields. MS 1000 shows good wetting and penetration results of glass fabric and therefore is well-suited for laminating glass, aramid and carbon fibre for the production of fibre-reinforced components. It can also be easily combined with different fillers (powdery, fibrous, fabric).
| Curing Characteristics | |
|---|---|
| Pot life at 20 °C (500 g batch) | ~80 min |
| Additional layer after (35% strength) | 9 h |
| Working strength after (80% strength) | 14 h |
| Final strength (100% strength) | 24 h |
| Shrinkage | 0.01% |
| Mechanical Properties (Cured at 24 h RT + 4 h @ 60 °C) | |
| Tensile strength (DIN EN ISO 527-2) | 56 MPa |
| Elongation at break (tensile) | 2.8% |
| E-modulus (tensile) | 2500–2600 MPa |
| Compressive strength (DIN EN ISO 604) | 92 MPa |
| Bending strength (DIN EN ISO 178) | 90 MPa |
| Hardness (Shore D, DIN ISO 7619) | 81 ± 3 |
| Taber Test (DIN ISO 9352, H18, 1 kg, 1000 rotations) | 1.1 g / 1.0 cm³ |
| Lap Shear Strength (Material Thickness 1.5 mm, DIN EN 1465) | |
| Steel 1.0338 (sandblasted) | 16 MPa |
| Stainless steel V2A (sandblasted) | 14 MPa |
| Aluminium (sandblasted) | 8 MPa |
| Galvanized steel | 7 MPa |
| Thermal Parameters | |
| Temperature resistance | -35 °C to +120 °C |
| Glass transition (Tg, room temp.) | ~+47 °C |
| Glass transition (Tg, after tempering at 70 °C) | +62 °C |
| Heat deflection resistance (DIN EN ISO 75-2) | +52 °C |
| Thermal conductivity (DIN EN ISO 22007-4) | 0.19 W/m·K |
| Heat capacity (DIN EN ISO 22007-4) | 1.21 J/(g·K) |
| Electrical Parameters | |
| Resistance (DIN EN 62631-3-1) | 2.31·10¹⁴ Ω·m |
| Magnetic | No |