WEICON WR2 is a pasty wear protection and is particularly suitable for areas where the processing of casting compounds is not possible such as the repair of conveyors, guide rails and sliding ways. The epoxy resin system is also used to prevent wear on metal surfaces that are subject to high abrasion and erosion. It can serve as a wear-resistant underlayer before the final coating with WEICON Ceramic BL WR2 can be used in mechanical and plant engineering, in equipment engineering, and in many other areas of industry.
LOCTITE® PC 7222 is a gray, two-part, epoxy-based surface coating putty designed to protect surfaces from severe wear, erosion, or cavitation, containing ceramic. It will not sag or shrink and can be used on overhead and vertical surfaces, conforming to irregular shapes. It provides a smooth, low-friction finish.
- For surfaces exposed to severe wear
- No shrinkage or sagging
- Can be used on overhead and vertical surfaces
- Conforms to irregular shapes
| WEICON SPESIFICATION | |
| Base | Epoxy |
| Filler | Mineral |
| Consistency | Paste |
| Shade | Anthracite |
| Processing Temperature | Component temperature > 3 °C above dew point |
| Relative Humidity | < 85 % |
| Mixing Ratio by Weight | 100:33 |
| Mixing Ratio by Volume | 100:27 |
| Viscosity of Mixture at +25°C | 560,000 mPa·s |
| Density of Mixture | 1.9 g/cm³ |
| Consumption (Layer thickness 1.0 mm) | 1.9 kg/m² |
| Maximum Layer Thickness per Work Step | 20 mm |
| Processing Time at 20 °C, 500 g batch | 30 min |
| Additional Layer After (35 % strength) | 4 h |
| Working Strength After (80 % strength) | 5 h |
| Final Strength (100 % strength) | 12 h |
| Shrinkage | 0.04 % |