WEICON 10013464 TI (Titanium) Epoxy Resin (0.5Kg)
WEICON TI has high pressure resistance and very resistant to chemicals. It is suitable especially for repair of pumps, valves, wearing plates, ball bearing seats, shafts, and propellers as well as for lining pump housings, slide bearings, etc. The epoxy resin system can be used in machine and system construction, in apparatus engineering and in many other industrial areas.
Specification
Name
WEICON 10013464 TI (Titanium) Epoxy Resin (0.5Kg)
SKU
4024596016784
Brand
Condition
New
| Material Properties (after curing at 24h RT + 14h at +150 °C) | |
|---|---|
| Mechanical Properties | |
| Tensile strength (DIN EN ISO 527-2) | 53 MPa |
| Elongation at break (DIN EN ISO 527-2) | 0.9 % |
| E-modulus (tensile) (DIN EN ISO 527-2) | 6200–6800 MPa |
| Compressive strength (DIN EN ISO 604) | 66 MPa |
| Bending strength (DIN EN ISO 178) | 10 MPa |
| Impact strength (DIN EN ISO 179-1/1eU) | 1.7 kJ/m² |
| Hardness (Shore D, DIN ISO 7619) | 83±3 |
| Adhesive strength (DIN EN ISO 4624) | 5 MPa |
| Taber Test (DIN ISO 9352, H18, 1kg, 1000 rotations) | 0.7 g / 0.4 cm³ |
| Lap shear strength (DIN EN 1465, 1.5 mm thickness) | |
| • Steel 1.0338 sandblasted | 5 MPa |
| • Stainless steel V2A sandblasted | 3 MPa |
| • Aluminium sandblasted | 3 MPa |
| • Galvanized steel | 4 MPa |
| Thermal Properties | |
| Temperature resistance | -35 to +200 °C (briefly up to +260 °C) |
| Tg after curing at RT (DSC) | ~ +52 °C |
| Tg after tempering at 150 °C (DSC) | +148 °C |
| Heat deflection resistance (DIN EN ISO 75-2, after tempering) | +150 °C |
| Electrical Properties | |
| Resistance (DIN EN 62631-3-1) | 1.7·10¹³ Ω·m |
| Magnetic | No |
| Approvals / Guidelines | |
| ISSA Code | 75.509.22/23 |
| IMPA Code | 812945/46 |
| MIL-Spec | Comply with MIL-C-24176 |